HDPE KRM Black - For Extrusion Pipes and Blow Moulding Pipes
HDPE KRM 100
High Density Polyethylene
HDPE KRM 100 is a high density polyethylene compound (Black) produced by the ultimate Koremplast technology. Antioxidants and processing stabilizers are added, for good oxidation resistance and high mechanical properties. Carbon black gives outstanding UV resistance.
Application: Extrusion (pipes not in pressure)
Informative Tensile properties in accordance to EN ISO 527
- Tensile strain at break (%) 700 - 950 Informative
- Tensile strength at Yeld (Mpa) 22 - 28 Informative
- Tensile strength at break (Mpa) 24 - 30 Informative
- Tensile Modulus (Mpa) 800 - 1200 Informative
| PROPERTY | METHOD | UNIT | RANGE | NOTE |
|---|---|---|---|---|
| M.F.I.(5 Kg) | ISO 1133 | g/10 min | 0.40-0.70 | guaranteed |
| Density | ISO 1183 | g/cm3 | 0.955-0.965 | guaranteed |
| Carbon Black | ISO 6964 | % | 2.00-2.50 | guaranteed |
| O.I.T. | EN 728 | min. | >20 | guaranteed |
HDPE KRM 95
High Density Polyethylene
HDPE KRM 95 is a high density polyethylene compound (Black) produced by the ultimate Koremplast technology. Antioxidants and processing stabilizers are added, for good oxidation resistance and high mechanical properties. Carbon black gives outstanding UV resistance.
Application: Extrusion (pipes not in pressure)
Informative Tensile properties in accordance to EN ISO 527
- Tensile strain at break (%) 650 - 950 Informative
- Tensile strength at Yeld (Mpa) 21 - 26 Informative
- Tensile strength at break (Mpa) 23 - 28 Informative
- Tensile Modulus (Mpa) 800 - 1150 Informative
| PROPERTY | METHOD | UNIT | RANGE | NOTE |
|---|---|---|---|---|
| M.F.I.(5 Kg) | ISO 1133 | g/10 min | 0.40-0.70 | guaranteed |
| Density | ISO 1183 | g/cm3 | 0.955-0.965 | guaranteed |
| Carbon Black | ISO 6964 | % | 2.00-2.50 | guaranteed |
| O.I.T. | EN 728 | min. | >20 | guaranteed |
HDPE KRM 90
High Density Polyethylene
HDPE KRM 90 is a high density polyethylene compound (Black) produced by the ultimate Koremplast technology. Antioxidants and processing stabilizers are added, for good oxidation resistance and high mechanical properties. Carbon black gives outstanding UV resistance.
Application: Extrusion (pipes not in pressure)
Informative Tensile properties in accordance to EN ISO 527
- Tensile strain at break (%) 650 - 950 Informative
- Tensile strength at Yeld (Mpa) 20 - 25 Informative
- Tensile strength at break (Mpa) 22 - 28 Informative
- Tensile Modulus (Mpa) 800 - 1100 Informative
| PROPERTY | METHOD | UNIT | RANGE | NOTE |
|---|---|---|---|---|
| M.F.I.(5 Kg) | ISO 1133 | g/10 min | 0.35-0.75 | guaranteed |
| Density | ISO 1183 | g/cm3 | 0.952-0.965 | guaranteed |
| Carbon Black | ISO 6964 | % | 2.00-2.50 | guaranteed |
| O.I.T. | EN 728 | min. | >20 | guaranteed |
HDPE KRM 80
High Density Polyethylene
HDPE KRM 80 is a high density polyethylene compound (Black) produced by the ultimate Koremplast technology. Carbon black gives outstanding UV resistance.
Application: Extrusion (pipes not in pressure)
Informative Tensile properties in accordance to EN ISO 527
- Tensile strain at break (%) 650 - 950 Informative
- Tensile strength at Yeld (Mpa) 20 - 25 Informative
- Tensile strength at break (Mpa) 22 - 28 Informative
- Tensile Modulus (Mpa) 800 - 1100 Informative
| PROPERTY | METHOD | UNIT | RANGE | NOTE |
|---|---|---|---|---|
| M.F.I.(5 Kg) | ISO 1133 | g/10 min | 0.35-0.75 | guaranteed |
| Density | ISO 1183 | g/cm3 | 0.952-0.965 | guaranteed |
| Carbon Black | ISO 6964 | % | 2.00-2.50 | guaranteed |
HDPE KRM 60
High Density Polyethylene
HDPE KRM 60 is a high density polyethylene compound (Black) produced by the ultimate Koremplast technology. Carbon black gives outstanding UV resistance.
Application: Extrusion/Blow Moulding (pipes not in pressure)
| PROPERTY | METHOD | UNIT | RANGE | NOTE |
|---|---|---|---|---|
| M.F.I.(2.16 Kg) | ISO 1133 | g/10 min | 0.20-0.45 | guaranteed |
| Density | ISO 1183 | g/cm3 | 0.955-0.972 | guaranteed |
| Carbon Black | ISO 6964 | % | 2.00-3.00 | guaranteed |